MATTE
FILM
This MH type polyester film possesses high haze, high gloss and
excellent muted and grainy surface characteristics. The film has
good dimensional stability at high temperatures. The film has
excellent processability and is suitable for printing, packaging,
metallisation, thermal lamination, labelling and graphics applications.
|
TECHNICAL
DATA Type – MH
|
| PROPERTY |
TEST METHOD
|
UNIT |
NOMINAL VALUE
|
| PHYSICAL |
|
|
|
|
|
|
|
| Thickness |
Internal |
micron
|
19 |
23 |
50 |
75 |
100 |
| Yield |
Internal |
m2/kg |
37.6 |
31.0 |
14.3 |
9.5 |
7.1 |
| Tensile
Strength at Break MD |
ASTM-D-882 |
kg/cm2 |
1900 |
2100 |
1700 |
1700 |
1600 |
|
TD |
|
|
2000 |
2000 |
2100 |
1900 |
1800 |
| Elongation
at Break MD |
ASTM-D-882 |
% |
90 |
100 |
130 |
130 |
150 |
|
TD |
|
|
85 |
110 |
90 |
125 |
110 |
| Co-efficient
of Static |
ASTM-D-1894 |
|
0.32 |
0.35 |
0.35 |
0.30 |
0.35 |
| Friction
Kinetic |
|
|
0.30 |
0.30 |
0.33 |
0.28 |
0.30 |
| OPTICAL |
|
|
|
|
|
|
|
| Haze |
ASTM-D-1003 |
% |
75 |
75 |
90 |
92 |
95 |
| Transmittance |
ASTM-D-1003 |
% |
75 |
70 |
75 |
75 |
70 |
| Gloss
20Deg |
ASTM-D-2457 |
% |
67 |
66 |
69 |
67 |
65 |
| 45
Deg |
|
|
25 |
35 |
25 |
24 |
25 |
| 60
Deg |
|
|
78 |
76 |
78 |
75 |
73 |
| THERMAL |
|
|
|
|
|
|
|
| Shrinkage
at 150 o C/30 MD |
ASTM-D-1204 |
% |
2.0 |
2.0 |
1.6 |
1.6 |
1.4 |
| minutes
TD |
|
|
1.5 |
1.5 |
1.0 |
1.0 |
0.8 |
MD- Machine Direction ; TD – Transverse Direction
UmaPETÒis the registered trademark for Ester Industries’
bi-axially oriented polyester films based on polyethylene terephthalate.
The information contained herein is to be used only as a guide for
using UmaPET film. The specifications and characteristics mentioned
are based on reliable test procedures. Users of this film should
make independent assessment of its suitability to their end use.
Ester Industries does not offer any guarantee on the results and
does not accept any liability arising out of the use of the information
contained herein.
|